Graphene ink for spin/spray coating photonically annealable
ALDRICH/900960 - for spin-coating, spray-coating, photonic annealing
Synonym: Conductive ink; Graphene ink
Product Type: Chemical
This image is provided for informative purposes only and does not represent an actual product label. It should not be used as a substitute for official product labeling.
| bp | 78 °C (ethanol) |
| concentration | 1.8-3.0 wt. % solids |
| density | 0.78-0.88 g/mL at 25 °C |
| form | dispersion (black) |
| greener alternative category |  , Enabling |
| greener alternative product characteristics | Design for Energy Efficiency Learn more about the Principles of Green Chemistry . |
| particle size | ≤3 μm |
| Quality Level | 100 |
| resistivity | 0.003-0.005 Ω-cm, sample prepared by spin-coating at 2000 rpm/30 s for 5 coats, followed by thermal annealing at 300 °C in air for 30 minutes |
| sustainability | Greener Alternative Product |
| viscosity | 2-8 mPa.s(25 °C) (1000 s-1) |
| Application: | Spin-coating: Spin-coating a single layer at 2000-5000 rpm yields a final film thickness of 40-60 nm. To achieve thicker films, multiple layers can be applied without a baking step. This is recommended over using a lower spin speed to maintain film uniformity. This ink should work on almost any substrate. Electrical performance: Following a baking step at 300 °C for 30 minutes in air, the spin-coated films exhibit sheet resistance of 300-800 Ω/sq, corresponding to a resistivity of 0.003-0.004 Ω−cm. With 5 coats at 2000 rpm, a 200 nm thick film with a sheet resistance of 160 Ω/sq. is obtained. General guidelines: Ethanol is recommended for cleaning up the ink and dried films, as well as dilution. Bath sonication (5-10 minutes) of the ink prior to use is recommended following extended periods of disuse. |
| General description: | We are committed to bringing you Greener Alternative Products, which adhere to one or more of The 12 Principles of Greener Chemistry. This product belongs to Enabling category of greener alternatives thus aligns with "Design for energy efficency". Graphene inks are highly conductive, low cost and super flexible. Click here  for more information. |
| Symbol |   GHS02,GHS05 |
| Signal word | Danger |
| Hazard statements | H225 - H318 |
| Precautionary statements | P210 - P280 - P305 + P351 + P338 + P310 - P370 + P378 - P403 + P235 |
| RIDADR | UN 1993BE 3 / PGII |
| WGK Germany | WGK 3 |
| Flash Point(F) | 54.5 °F - closed cup |
| Flash Point(C) | 12.5 °C - closed cup |
| bp | 78 °C (ethanol) |
| Density | 0.78-0.88 g/mL at 25 °C |
| UNSPSC | 12141908 |